33x33x2mm Steel Equal Angle
33x33x2mm Steel equal angle in S235JR–S355J2, ASTM A36 to EN 10056-1 / ASTM A6, with an uncoated steel surface suitable for further processing or painting. Nominal weight 1.03 kg/m.
Minimum order
Minimum 5 t per size. Standard length 6 m; other lengths on request. We confirm the grade, tolerances and lead time in your quote.
Add to Quote Request
Select length and quantity to add to your quote cart
Minimum order: 813 pieces
Minimum order: 5,000 kg per size
Applications & Usage
Typical uses for this equal angle: trim, light framing, display systems and interior fit-out. Wall thickness 2 mm: suited to light loads. Supplied in the bare mill finish, without coating, which keeps cost down where appearance is secondary. Standard lengths: 6m.
Technical Specifications
| Specification | Value |
|---|---|
| Dimensions | 33mm × 33mm × 2mm |
| Weight per Meter | 1.026 kg/m |
| Weight of a 6 m length | 6.2 kg |
| Material | Steel |
| Alloy/Grade | S235JR, S275JR, S355JR, S355J2, ASTM A36, ASTM A572, ASTM A615, SAE 1010, SAE 1020, SAE 1030, SAE 1035, SAE 1040, SAE 1045, SAE 1060, ST 37-2, ST 44-2, ST 52-3, ST 60 |
| Standard | EN 10056-1 / ASTM A6 |
| Available Lengths | 6m |
| Full Stock Length | 6 m |
| Minimum Order per Size | 5 t |
Section Properties
Indicative values calculated from nominal dimensions; root and toe radii are taken from EN 10056-1 and interpolated for intermediate legs. Length per tonne from the catalogue mass.
| Property | Value |
|---|---|
| Cross-sectional area(A) | 1.32 cm² |
| Centroid distance(e) | 0.867 cm |
| Second moment of area(Ix = Iy) | 1.34 cm⁴ |
| Elastic section modulus(Wel) | 0.552 cm³ |
| Radius of gyration(ix = iy) | 1.01 cm |
| Second moment of area(Iu) | 2.12 cm⁴ |
| Radius of gyration(iu) | 1.27 cm |
| Second moment of area(Iv) | 0.568 cm⁴ |
| Radius of gyration(iv) | 0.656 cm |
| Surface area per metre(As) | 0.128 m²/m |
| Length per tonne | 975 m |
Grades and mechanical properties
Minimum values for a governing thickness of 2 mm.
| Grade | Min. yield | Tensile strength | Min. elongation A (%) | Impact test (KV) |
|---|---|---|---|---|
| S235JREN 10025-2 | 235 MPa | 360–510 MPa | — | — |
| S275JREN 10025-2 | 275 MPa | 430–580 MPa | — | — |
| S355JREN 10025-2 | 355 MPa | 510–680 MPa | — | — |
| S355J2EN 10025-2 | 355 MPa | 510–680 MPa | — | — |
| ASTM A36 | 250 MPa (36 ksi) | 400–550 MPa (58–80 ksi) | — | — |
| ASTM A572 Gr. 50 | 345 MPa (50 ksi) | ≥ 450 MPa (≥ 65 ksi) | — | — |
SAE 1010–1060 and the ST 37-2 to ST 60 designations are supplied to chemical composition; their mechanical properties depend on the delivery condition and are confirmed per order. ASTM A615 is a reinforcing-bar standard, quoted on request. Impact values apply from 6 mm; for thin sections (EN below 3 mm, ASTM below 8 mm) the elongation requirement follows separate rules and is given in the test certificate. ASTM A572 values are for Grade 50; please confirm the grade in your enquiry.
Similar Sizes
Explore alternative dimensions that might suit your needs
Technical guides
Structural steel grades: S235JR, S275JR, S355JR, S355J2 and ASTM A36, A572 and A992 compared
Minimum yield and tensile strength, impact test temperatures and carbon equivalent of EN 10025-2 grades S235JR, S275JR, S355JR and S355J2, the old St37 and St52 names, and how ASTM A36, A572 Grade 50 and A992 compare.
Read the guide →Steel bar weight chart: flat, round, square and hexagon bar and equal angles (kg/m)
Weight per metre of steel flat, round, square and hexagon bar and equal angles 18×18 to 120×120, with the formulas behind each table and the weight of a 6 m bar.
Read the guide →Angle sizes and weights: steel, stainless and aluminium equal and unequal angles
Weight per metre and cross-section area of hot-rolled equal steel angles to EN 10056-1 from 20 × 20 × 3 to 120 × 120 × 12, plus stainless 304 and aluminium 6063 angles, the kg/m formula and how angles are designated.